The main raw materials of JKN-AGM-800S oil well cement are styrene butadiene latex, butadiene styrene and styrene as main monomers, which are prepared by emulsion polymerization.
Inquiry
Product Description
The main raw materials of JKN-AGM-800S oil well cement are styrene butadiene latex, butadiene styrene and styrene as main monomers, which are prepared by emulsion polymerization. The latex of JKN-AGM-800S oil well cement has good chemical stability and mechanical stability, and has good anti gas channeling performance in the process of cement slurry.
Characteristics
JKN-AGM-800S is made of styrene butadiene latex mainly.
Good anti gas channeling performance.
Has good compatibility with various of oil well cements and other additives .
Has good salt tolerance, can be applied to salt water slurry.
Can significantly reduce the amount of water reducing agent with reducing water loss property.
Normal dosage: 3%～10%(BWOS).
Has good stability,not easy to demulsificate.Free fluid is near to zero.
Cement slurry thickening transition time is short, close to right angle thickening.
Technical Specification
Items | Specification |
Appearance | Free flowing powder |
Initial consistrency(80℃,46.5MPa,45min),Bc | ≤30.0 |
Sudden change value of consistency | ≤10.0 |
40Bc ~ 100Bc time,min | ≤40.0 |
Fluid loss(80℃,6.9MPa,30min),ml | ≤100.0 |
Compression strength(102℃,21MPa,24h),MPa | ≥14.0 |
Packing, Storage
The solid be sacked with three-layer plastics bag, 25kg per bag.
Be kept away from moisture and possible damage of the packages in transportation, be stored in cool and dry situation.
Storage life time is two years.